Tough 2000
Formlabs Tough 2000 TDS
Formlabs Tough 2000 Resin 1L | Dynamism
asset.dynamism.com
Full PDF Document
If the inline viewer fails, it will open the original document in compatibility mode automatically. You can also open the file directly.
Extracted Text
ENGINEERING RESIN Tough 2000 Tough 2000 Resin for Rugged Prototyping Tough 2000 Resin is the strongest and stiffest material in our functional family of Tough and Durable Resins. Choose Tough 2000 Resin for prototyping strong and sturdy parts that should not bend easily. Strong and stiff prototypes ABS-like strength and stiffness Sturdy jigs and fixtures V1 FLTO2001 Prepared 03 . 02 . 2020 Rev 01 03 . 02 . 2020 To the best of our knowledge the information contained herein is accurate. However, Formlabs, Inc. makes no warranty, expressed or implied, regarding the accuracy of these results to be obtained from the use thereof. Tough 2000 Resin Material Properties Data Mechanical Properties Ultimate Tensile Strength Tensile Modulus Elongation at Break Flexural Properties Flexural Strength Flexural Modulus Impact Properties Notched IZOD Unnotched IZOD Thermal Properties Heat Deflection Temp. @ 1.8 MPa Heat Deflection Temp. @ 0.45 MPa Coefficient of Thermal Expansion METRIC1 Green2 Post-Cured3 IMPERIAL1 Green2 Post-Cured3 29 MPa 1.2 GPa 74 % 46 MPa 2.2 GPa 48 % 4206 psi 174 ksi 74 % 6671 psi 329 ksi 48 % 17 MPa 0.45 GPa 65 MPa 1.9 GPa 2465 psi 65 ksi 9427 psi 275 ksi 79 J/m 208 J/m 40 J/m 715 J/m 1.5 ft-lbf/in 3.9 ft-lbf/in 0.75 ft-lbf/in 13 ft-lbf/in 42 �C 48 �C 107 �m/m/�C 53 �C 63 �C 91 �m/m/�C 108 �F 118 �F 59 in/in/�F 127 �F 145 �F 50 in/in/�F METHOD ASTM D 638-14 ASTM D 638-14 ASTM D 638-14 ASTM D 790-15 ASTM D 790-15 ASTM D256-10 ASTM D4812-11 ASTM D 648-16 ASTM D 648-16 ASTM E 831-13 1 M aterial properties can vary with part geometry, print orientation, print settings, and temperature. 2 D ata was obtained from green parts, printed using Form 2, 100 m, Tough settings, washed and air dried without post cure. 3 D ata was obtained from parts printed using Form 2, 100 m, Tough 2000 settings, and postcured with a Form Cure for 120 minutes at 80 �C. Solvent Compatibility Percent weight gain over 24 hours for a printed and post-cured 1 x 1 x 1 cm cube immersed in respective solvent: Solvent 24 Hour Weight Gain (%) Acetic Acid, 5 % 0.71 Acetone 18.82 Isopropyl Alcohol 3.7 Bleach, ~5 % NaOCl 0.56 Butyl Acetate 6.19 Diesel 0.06 Diethyl glycol monomethyl ether 5.32 Hydrolic Oil 0.08 Skydrol 5 0.87 Solvent Hydrogen Peroxide (3 %) Isooctane Mineral Oil, light Mineral Oil, heavy Salt Water (3.5 % NaCl) Sodium hydroxide (0.025 %, pH = 10) Water Xylene Strong Acid (HCI Conc) 24 Hour Weight Gain (%) 0.63 0.03 0.13 0.17 0.56 0.61 0.61 4.1 3.01